Surface enhanced Raman scattering (SERS) investigation of amorphous carbon
Veres, M ✉ [Veres, Miklós (Optika, Raman-spe...), szerző] Amorf vékonyrétegek (SZFKI)
;
Füle, M [Füle, Miklós Jenő (Lézerfény-anyag k...), szerző] KFKI Szilárdtestfizikai és Optikai Kutató Intézet
;
Tóth, S [Tóth, Sára (Szén szerkezetek,...), szerző] Amorf vékonyrétegek (SZFKI)
;
Koós, M [Koós, Margit (Amorf félvezetők,...), szerző] Amorf vékonyrétegek (SZFKI)
;
Pócsik, I [Pócsik, István, szerző] Lézeralkalmazási Osztály (SZFKI)
Angol nyelvű Szakcikk (Folyóiratcikk) Tudományos
Megjelent:
DIAMOND AND RELATED MATERIALS 0925-9635 1879-0062
13
(4-8)
pp. 1412-1415
2004
SJR Scopus - Electrical and Electronic Engineering: D1
Azonosítók
MTMT: 144111
DOI:
10.1016/j.diamond.2004.01.041
WoS:
000221691100167
Scopus:
2442495059
Szakterületek:
Fizika
Surface enhanced Raman scattering (SERS) was applied to study hydrogenated amorphous carbon (a-C:H) and amorphous carbon (a-C) samples. Carbon free silver colloid served as SERS active medium; it was dried on the sample surface. The Raman signal amplitude increase by order of magnitude was observed. Further enhancement was recorded on the Raman spectrum as a result of the blinking phenomenon, which took place applying certain measurements conditions. A number of reproducible peaks was observed in the D and G band region both for a-C:H and a-C. Coexistence of these peaks in one sample's spectrum indicates that the amorphous carbon D and G peaks consist of several components: they are inhomogeneously broadened. For a given amorphous carbon sample the shape of the conventional Raman spectrum is determined by vibrations of dominant structural units. SERS gives the possibility to identify these units; moreover, presence of other components, not so characteristic for the sample, also can be evaluated. © 2004 Elsevier B.V. All rights reserved.
Idézők (73)
Idézett közlemények (3)
Hivatkozás stílusok:
IEEE
ACM
APA
Chicago
Harvard
CSL
Másolás
Nyomtatás
2025-01-04 06:28
×
Lista exportálása irodalomjegyzékként
Hivatkozás stílusok:
IEEE
ACM
APA
Chicago
Harvard
Nyomtatás
Másolás